Structural,Spectral and Electrical Properties of BaNi2-xZnxFe16O27 Nanoparticles Ferrites
الكلمات المفتاحية:
Barium ferrite، Band gaps، Fourier transforms infrared، AC conductivity، Zinc substitutionالملخص
In the current study, w-type BNF-NPs synthesis via ceramic method.the effects of zinc ions doping on the physical properties of BNF-NPs were analyzed. The formation of BNF-NPs emphasized by XRD, FTIR, UV-Visible spectroscopy and electrical conductivity measurement. The phases structure , crysttallite size and lattice parameters wrere evaluated using XRD results. Hexagonal structure with a single phase apeares, the average grain size was found to be in Nano scale from 32 to 34 nm, while the lattice parameters increased slolly as the doping concentration of zinc ions increases. The spectra of FTIR showed main absorption bands which confirmed formation of hexagonal ferrite phase. UV-VIS analysis was also performed and found that the band gaps were in the semiconducting region and increased with increasing zinc concentration. The AC conductivity of the samples decreased with increasing zinc content and showed a dependence on the frequency and temperature. Additionally, as frequency increase the σac conductivity showed dispersion that decreased as temperature increased.
التنزيلات
منشور
كيفية الاقتباس
إصدار
القسم
الحقوق الفكرية (c) 2023 Sadiq.H Khoreem، Abdual-hakeem AL-Hammadi
هذا العمل مرخص بموجب Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.